Effect of cutting speed on the surface integrity of face milled 7050-T7451 aluminium workpiecesAuthor
Published Date
2018Publisher
Elsevier Ltd.Keywords
aluminium alloysmilling
Surface Integrity
Abstract
The guarantee of surface integrity has become a primary objective for researchers when analysing the reliability of machined aircraft aluminium alloy structural parts in high-speed machining. This wor ... [+]
The guarantee of surface integrity has become a primary objective for researchers when analysing the reliability of machined aircraft aluminium alloy structural parts in high-speed machining. This work studies the effect of cutting speed on the surface integrity of face milled 7050-T7451 aluminium workpieces. First, 7050-T7451 aluminium workpieces were face milled under dry conditions using three cutting speeds (200, 800, 1400 m/min) at constant feed (0.20 mm/tooth) and depth of cut (1 mm). An indexable face milling cutter with a diameter of 50 mm with five uncoated inserts was used in the face milling tests. During the machining process, cutting forces were acquired employing a Kistler dynamometer in order to understand the influence of the mechanical load on the final surface quality. The surface roughness p roduced by the milling process was measured using a portable rugosimeter. The residual stresses generated by the cutting process were measured by the holedrilling technique. In addition, small specimens were cut out from the workpieces and microstructural alterations of the surface layer were analysed employing optical microscopy techniques. The results demonstrate that the magnitude of residual stresses and the thickness of the affected layer is sensitive to the cutting speed, while surface roughness and microstructural defects do not show significant variations for the tested conditions. [-]
Publisher’s version
https://doi.org/10.1016/j.procir.2018.05.034ISSN
2212-8271Published at
Procedia CIRP Vol. 71Document type
Article
Version
Published
Rights
© 2018 The AuthorsAccess
Open AccessCollections
- Articles - Engineering [483]
The following license files are associated with this item: